24UT0325
利用課題名 / Title
Tandem NH3-SCR catalyst based on Cu- and Fe- containing zeolite
利用した実施機関 / Support Institute
東京大学 / Tokyo Univ.
機関外・機関内の利用 / External or Internal Use
内部利用(ARIM事業参画者以外)/Internal Use (by non ARIM members)
技術領域 / Technology Area
【横断技術領域 / Cross-Technology Area】(主 / Main)計測・分析/Advanced Characterization(副 / Sub)-
【重要技術領域 / Important Technology Area】(主 / Main)次世代ナノスケールマテリアル/Next-generation nanoscale materials(副 / Sub)-
キーワード / Keywords
catalyst,ナノ多孔体/ Nanoporuous material,電子分光/ Electron spectroscopy
利用者と利用形態 / User and Support Type
利用者名(課題申請者)/ User Name (Project Applicant)
兪 敬允
所属名 / Affiliation
東京大学大学院工学系研究科化学システム工学専攻
共同利用者氏名 / Names of Collaborators in Other Institutes Than Hub and Spoke Institutes
ARIM実施機関支援担当者 / Names of Collaborators in The Hub and Spoke Institutes
沖津康平
利用形態 / Support Type
(主 / Main)機器利用/Equipment Utilization(副 / Sub)-
利用した主な設備 / Equipment Used in This Project
UT-308:多機能走査型X線光電子分光分析装置(XPS)with AES
報告書データ / Report
概要(目的・用途・実施内容)/ Abstract (Aim, Use Applications and Contents)
The topic is to study zeolite catalysts for selective catalytic reduction of NOx with NH3. XPS can analyze the chemical states of metal species such as Cu and Fe in the mono-metal loaded and bi-metal loaded samples and help understand how it will further affect the catalytic performance as active sites.
実験 / Experimental
Cu-beta, Fe-beta and CuFe-beta (metal content around 1.5wt%) powder and pellet samples are prepared for XPS measurement(VersaProbe III).
結果と考察 / Results and Discussion
For powder samples, there is almost no
signal of metal elements because of the thickness of the sample.
For pellet samples, though there is very low signal for Fe (around 710.8eV) and
Cu (around 933.6eV), it is hard to make a further analysis due to the low
signal-to-noise ratio.
In the future, we will try to measure the samples again with more scan loops to
increase the signal-to-noise ratio or try to use the transfer vessel to prevent
the contamination from carbon in the atmosphere as much as possible, and
analyze the results by combining with other characterization such as H2-TPR
or EXAFS.
図・表・数式 / Figures, Tables and Equations
その他・特記事項(参考文献・謝辞等) / Remarks(References and Acknowledgements)
成果発表・成果利用 / Publication and Patents
論文・プロシーディング(DOIのあるもの) / DOI (Publication and Proceedings)
口頭発表、ポスター発表および、その他の論文 / Oral Presentations etc.
特許 / Patents
特許出願件数 / Number of Patent Applications:0件
特許登録件数 / Number of Registered Patents:0件